重铁锈垢(磁性铁锈Fe3O4垢)专用清洗剂(一)

刘含雷1,吕刚2,商海智3,李爱兵1,田民格1

1. 济宁新格瑞水处理有限公司,山东济宁 2724152. 酒泉钢铁(集团)有限公司,甘肃嘉峪关 7351003. 山东省特种设备检验研究院济宁分院,山东济宁)

摘要 本文介绍了一种磁性铁锈垢(Fe3O4)专用清洗剂SGR-1302,并考察了清洗剂浓度、温度、体系PH等因素对清洗效果的影响。通过实验得出较为合理的清洗剂用量15-25 wt%,清洗温度≤80℃清洗液PH1.5-2.5,清洗时间6h-24h。在添加缓蚀剂SGR-0405条件下,对A3碳钢、G20钢腐蚀性安全。并且SGR-1302在工业清洗中除垢率满足客户要求。

关键词 Fe3O4;清洗剂;SGR-1302

Study on the application of SGR-1302 iron oxide(Fe3O4) scale cleaner

LIU Hanlei1, LV Gang2, SHANG Haizhi3, LI Aibing1, TIAN Minge1

(1. Jining Scientific green water treatment Co., Jining, Shandong 272415; 2. Jiuguan Iron Steel Group, Jiayuguan, Gansu 735100; 3. Jining branch of Shandong Special Equipment Inspection Institute, Jining, Shandong 272000, China)

Abstract: In this paper, the application property on SGR-1302 iron oxide(Fe3O4) scale cleaner was studied via the SGR-1302 concentrationtemperature, PH and so on. The results indicated that the better chemical cleaning conditions were SGR-1302 concentration 15-20 wt%temperature ≤80℃, PH 1.5-2.5. On adding the corrosion inhibitor SGR-0405(0.3 wt%) into the chemical cleaning system, the rate of corrosions met the chemical cleaning demands on the A3 and G20 metal materials. And the SGR-1302 was successfully applied into MC system cleaning process.

Key words: Fe3O4; ckeaner; SGR-1302

1 前言  

    换热器内表面,比如锅炉水冷壁[1][2]、钢铁企业MC系统管道内壁等,常常会生成质地坚硬的黑色磁性铁垢(Fe3O4),严重影响系统换热效率,需要及时清除。化学清洗此类垢污常常采用两种处理方式:1)混合无机酸或有机酸[3],比如盐酸-氢氟酸等,通过离子价态转化、酸溶与螯合増溶而达到化学除垢目的;2)螯合剂清洗,主要通过螯合、改变污垢晶格而达到脱除垢污目的。混合无机酸,清洗操作要求比较严格,设备腐蚀控制是此类清洗弊端;采用混合有机酸,为达到较高清洗效率,清洗必须维持还原环境,所以常常引入大量还原剂,并且要求温度也比较高,一般90℃以上,现场控制比较严,但是对于大量磁性垢污的清洗效果也比较差,采用精品级有机酸成本也比较高。螯合清洗剂虽然能克服以上清洗方式对设备损伤、操作不好控制等的缺陷,但是清洗时间比较长、单位清洗费用比较高,并且清洗废液回用也比较麻烦。

在清洗实践与大量文献资料调研基础上,研究中心采用特殊螯合剂、增效剂、表面活性剂等成分合成一款高效重铁锈垢(磁性铁锈Fe3O4)专用清洗剂SGR-1302。SGR-1302使用简便、高效,可以短时间清除换热器设备表面大量铁垢。本文就SGR-1302的应用性能做进一步研究,并对清洗实践成果做简单介绍。